THE CRYSTALLIZATION OF GOLD, SILVER, AND OTHER METALS.
By THOMAS J. GREGAN.
THERE are few chemical experiments so well known as the growth of the "lead-tree" and "silver-tree." These carry our minds back to the times of the alchemists, who called the first "Arbor Saturni," and the second "Arbor Dianæ," and they may be looked upon as the type of a large number of phenomena in which the salt of one metal in solution is decomposed by some other metal.
My assistant, Dr. Hand, and myself have lately been experimenting on these replacements, the metallic crystals which are thus produced, and the forces that act through the liquid. Our more special attention has been given to the mutual action of copper and nitrate of silver. If these two substances be brought into contact by the intervention of water, there grows on the red metal what may be called "trees," and, though the analogy between the crystals and the plants is a very superficial one, still the resemblances of external form are sufficiently striking, and a nomenclature drawn from the garden seems the most expressive.
A microscopic view of the growth of these silver crystals round a piece of copper is a truly beautiful sight; a blue glass underneath increases the effect, but they are best seen when they reflect a strong light thrown upon them. They may also be thrown upon a screen as opaque objects, but the beauty and luster of their surfaces are in this way lost. The crystals of silver thus produced differ both in color and form according to the strength of the solution. If it be very weak—say one per cent.—the copper is fringed with black bushes of the metal, which in growing change color to white without any alteration of crystalline form that can be detected by a powerful microscope. A stronger solution gives white crystals from the commencement, which frequentlyassume the appearance of fern-leaves; while the growth from a still stronger liquid reminds us rather of a furze-bush. If the nitrate of silver amount to fifteen per cent, or thereabouts, there occurs a steady advance of brilliantly white moss; and, if the solution be saturated, or nearly so—say forty per cent.—this moss is very sturdy, often ending in solid crystalline knobs, or stretching out into the liquid as an arborescent fringe.
In all these cases, however, when the solution in front of the growing crystals has been somewhat exhausted, certain prominent or well-circumstanced crystals seem to monopolize the power, and to push forward through the remaining portions of the liquid. This raises beautiful branches which assume a variety of graceful forms, which it is hopeless to attempt to portray by diagrams, but the subjoined figures give some of the more characteristic outlines greatly magnified. The weak solutions produce feathery crystals, as somewhat in Fig. 1, consisting of
PSM V14 D451 Chemical crystallization of gold and silver 1.jpg
Fig. 1.Fig. 2.
a straight central stem from which grow on either side crystalline rays that terminate in a sharp point, and frequently become themselves the center stem of a similar crystalline structure.
In the outlying growth of a moderately strong solution the apparent regularity of the crystalline form is lost; the main stem is built of a confused mass of hexagonal plates, while the side branches are an agglomeration of minute pointed crystals turning in every direction, and producing such jagged outlines as in Fig 2.
PSM V14 D451 Chemical crystallization of gold and silver 2.jpg
Fig. 3.Fig. 4.
In still stronger solutions the branches lose every appearance of straightness, and they are built of hexagonal plates so studded with crystalline specks that the whole has the rounded appearance as in Fig. 3. The arborescent crystals that succeed the fringes, from a saturated solution, are smaller in their foliage than the last, and end in small spherical or botryoidal knobs.
Besides these various forms, there occur all kinds of crystalline combinations, as for instance the spray sketched in Fig. 4, when the long
170px
Fig. 5.
and rough branches have terminated each in a large hexagonal plate and the flowing past of a weak solution has afterward caused the growth of delicate fern-leaves. Often, also, a large expansion will take place in every direction, though joined to the parent stem by an almost invisible thread; or, from the point of a long crystal there will branch out to right and left crescent-shaped structures, a process the commencement of which is seen in one of the side rays of Fig. 1. The last traces of silver will frequently give rise to delicate crystalline filaments wandering over the surface of the glass, as in Fig. 5.
If a piece of zinc be placed in a solution of neutral terchloride of
PSM V14 D452 Chemical crystallization of gold and silver 2.jpg
Fig. 6.
gold, containing about nine per cent, of salt, there is an immediate out-growth of black gold, which speedily changes to an advancing mass of yellow or perhaps lilac metal of lichen-like forms, from which proceed beautiful fringes of yellow or black, ending generally in such arborescent forms as are represented in Fig. 6. As these branches push into the yellow liquid, it becomes colorless even in advance of their points, and it frequently happens that yellow crystals of some salt shoot out in front of the crystallizing metal, which follows them and builds up its advancing fronds at their expense. This is shown in the figure. The gold will generally shoot its yellow branches rapidly round the margin of the drop. Such a running branch has been seen to stop on coming in contact with a loose piece of gold, which immediately in its turn becomes active, and commences to sprout on its farther side. Copper salts give round nodules, which have no crystal-line appearance when deposited from moderately weak solutions, but a very strong solution of the chloride—about forty per cent.—yields with zinc, first a thick, black growth, then arborescent fringes of red metal, terminating in crystals of very appreciable size.
The fringes referred to in the case of these three metals are still more characteristically developed by bismuth.
170px
Fig. 7.
When a solution of the terchloride of bismuth acts on zinc there is an immediate outgrowth of black fringes, as in Fig. 7, where they are seen on an illuminated field. As they advance, these become more arborescent, and as the crystalline character becomes more developed they change from black to gray. Sometimes bismuth presents itself in botryoidal masses, but the tendency to form the fringes is very strong.
Chloride of antimony with zinc also gives black fringes. Lead salts yield crystals resembling those of silver, but leaves of irregular, hexagonal plates prevail, and frequently become of large size.
A solution of acetate of thallium, of twenty per cent, of salt, quickly gives a beautiful forest of thorny crystals. Sulphate of cadmium gives rise to a small, leaf-like growth on zinc; but a strong solution of the chloride produces an appearance of sticks covered with small spines or knobs. The new metal indium is thrown down upon zinc in the form of thick, white crystals. The deposition is promoted by touching the zinc with a piece of iron.
Tin gives beautiful results. If zinc be placed in a solution of stannous chloride it is quickly surrounded with a growth of prolonged octohedra, and as these advance into the liquid it is easy to observe that the additions of new metal commence at the apex, and that the wave of chemical change proceeds down the lateral edge, occupying some seconds of time in depositing the new layer of material. Frequently, also, there is a luxuriant growth of large, flat leaflets, or symmetrical structures resembling fern-leaves, but with the fronds arranged at right 
PSM V14 D454 Variance of crystallization by chemical concentration.jpg
Fig. 8.
angles, or combinations of these with octohedra, as shown in Fig. 8, These fern-leaves often begin of a dull-gray color, but, as they advance, suddenly change to a brilliant white. The particular form of these crystalline growths depends, therefore, primarily on the specific character of the metal, but this is greatly modified by the strength of the solution.
The forms assumed by native metals resemble those produced by the process of substitution. In some cases, indeed, it seems almost certain that the deposition of these minerals was effected in the same way—as, for instance, the silver on the native copper of the Lake Superior district.
Gold is frequently found in cubes more or less rolled, but the leaf-gold from Transylvania bears a striking likeness to the crystals that form in our laboratory experiments.
Silver is often found native as twisted hairs or wires of metal—a form that never occurs in the decomposition of its nitrate by copper, but which can be artificially produced in another way. There has been noticed a singular tendency in old silver ornaments and coins to become crystalline and friable. I have an ancient fibula from the island of Cyprus, supposed to be at least fifteen hundred years old, which, through the greater portion of its substance, presents a fracture something like that of cast iron, and its specific gravity has been reduced in round numbers from ten to nine.
It contains a little copper. This property of certain metals, or their alloys, to change in condition and in volume, is worthy the attention of those whose duty it is to make our standards. Experiments should be instituted for the purpose of learning what metals or combinations of metals are least subject to this secular change.
These metallic crystals are Nature's first attempt at building. The material is the simplest possible—in fact, what chemists look upon as elementary. But how is the building carried on? What are the tools employed? Where are the bearers of burdens that bring and prepare the pieces and lay them together according to the plan of the Great Architect? We must imagine what is taking place in the transparent solution. The silver, of course, existed at first in combination with the nitric element, and for every particle of silver deposited on the growing tree an equivalent particle of copper is dissolved from the surface of the plate. The nitric element never ceases to be in combination with a metal, but is transferred from the one metal to the other. On the "polarization theory" the positive and negative elements of the salt constantly change places and enter into fresh combination, one consequence of which would be a gradual passage of the nitric element from the growing silver to the copper plate. This actually takes place, and there is a diminution of the salt at the ends of the silver branches, giving rise to an upward current and a condensation of nitrate of copper against the copper plate, which gives rise to a downward current. These two currents are seen in every reaction of this nature. In the case of silver and copper, however, it has been proved that the crowding of the salt toward the copper plate is more rapid than would follow in the usual "polarization theory." The instrument used in determining this point was a divided cell in which two plates, one of silver and one of copper, connected with a wire, are each immersed in a solution of its own nitrate, contained in each division of the cell, and separated merely by parchment paper. The crystals of silver deposited on the silver plate in this experiment are very brilliant. There are indications of the liquid being put into a special condition by the presence of two metals which touch one another. Zinc alone is incapable of decomposing pure water, but if copper or platinum be deposited on the zinc in such manner that the water can have free access to the junction of the two metals, a decomposition is effected; oxide of zinc is formed and hydrogen gas is evolved. At ordinary temperature the bubbles of gas rise slowly through the liquid, but, if the whole be placed in a flask and heated, pure hydrogen is given off in large quantity. We have also found that iron or lead similarly brought into intimate union with a more electro-negative metal, and well washed, will decompose in pure water.
As might be expected, the action of magnesium on water may be greatly enhanced by this method; and a pretty and instructive experiment may be made by placing a coil of magnesium in pure water at the ordinary temperature, when there will be scarcely any visible effect, and, then adding a solution of sulphate of copper, the magnesium is instantly covered with a growth of the other metals, and at the same time the liquid seems to boil with the rapid evolution of the hydrogen bubbles from the decomposed water.
When, however, the force of the two metals in contact has to traverse a layer of water, the resistenceoffered by the fluid prevents its decomposition. This must also be an important element in the decomposition of a metallic salt dissolved in water—and, in fact, we have found that the addition of some neutral salt, such as nitrate of potassium, increases the action, apparently by diminishing the resistance of the liquid. If, too, we increase the quantity of the dissolved salt, we get more than a proportional increase of deposited metal. Thus, in an experiment made with different strengths of nitrate of silver, the following results were obtained in ten minutes, all the circumstances being the same except the strength of the solution:
1per cent.solution,0259copper.
2""078"
4""224"
In fact, it has been found that, in solutions not exceeding five per cent., twice the amount of nitrate of silver dissolved in water gives three times the amount of chemical action; and this is true with other metals also in weak solution. It may be that this is not the precise expression of a physical law, but it agrees at least closely with the results of experiment.
The power arising from this action of two metals on a binary liquid may be carried to a distance and produce similar decompositions there. This is ordinary electrolysis. Metals have often been crystallized from their solutions in this way, and I have seen excellent preparations of crystalline silver, gold, tin, copper, platinum, etc., by using poles of the same metal as that intended to be deposited upon them. The forms thus obtained are precisely analogous to those produced by the simple immersion of one metal into a soluble salt of another, and illustrate still further the essential unity of the force that originates the two classes of phenomena.
Popular Science Monthly, Volume 14, February 1879

Please help beat cancer - DONATE click above

 

A STEAMPUNK NOVEL, FULL OF
ANARCHIC EXPERIMENTAL SCIENCE


"Hodges emitted a scream the like of which
I hadn't heard since his scrotum was burned off
during my experiment with fluorine gas last year."


The Exotic Experimentation of Ernest Glitch,
Victorian Science with a Smile

More information & sample chapters here

Search for Ernest Glitch on your Kindle
or visit Amazon -
UK here
USA here


Unrelated to this post, below is an example of
eclectic science esoterica 

Antoine-Laurent Lavoisier




Main Menu - click above
WARNING - Many subjects outlined within this site are extremely dangerous and are provided here for information only. Please don`t experiment with high voltages or chemicals unless you are fully conversant with safe laboratory practices. No liability will be accepted for death, injury or damage arising from experimentation using any information or materials supplied.